Coating plasticization process Spray the prepared paint on the surface of the sample and put it in a constant temperature drying oven, and heat it to (60;80)°C (not more than 80°C, otherwise the coating will bubble due to excessive water evaporation), and keep it for 20 minutes; Then increase the temperature to 120°C and keep it for 20 minutes.

Molybdenum disulfide 2.3 NDZ-311W 0. The steps are as follows:

(1) Weigh the required concentrated PTFE dispersion and stir at high speed;

(2) Add the required amount of tin bronze powder, molybdenum disulfide, chromium trioxide, polyphenylene sulfide resin, and stir at high speed;

(3) Add titanate coupling agent NDZ-311W slowly and stir;

(4) PTFE BBQ Mat Slowly add Foamaster III defoamer and stir;

(5) Slowly add Levelling 620 associative levelling agent and stir;

(6) Slowly add the film-forming aid alcohol ester twelve and stir.

Preparation: Use concentrated polytetrafluoroethylene dispersion as the base material, and add fillers (the fillers are dried through a 600-mesh screen) and additives. Levelling620 0.006 Alcohol ester twelve 0.7 Bronze powder 6.

Formula 1 (Single-layer Teflon coating) Polytetrafluoroethylene concentrated dispersion 100 Chromium trioxide FoamasterIII 0. Take it out and put it in a box-type resistance furnace for plasticization.Polyphenylene sulfide.

Teflon coating, Teflon coating. To The high-tech performance of Teflon spraying can reduce product costs and improve production efficiency in many ways.

It can also be used to directly solve problems on your products to improve product quality and increase sales.Teflon spray is a unique industrial coating, it has excellent characteristics that other industrial coatings cannot match.

To Here we list some examples to show the advantages of using Teflon industrial coatings, so that you can understand the relationship between Teflon and your products, and let us share with you our experience in the application of Teflon to help you better Use our products well.

To Teflon industrial coatings are available in powder form and liquid form. Teflon PTFE, FEP, PFA, ETFE and Teflon-S may be the beginning of your next brilliant idea or the final solution to your problem.

The flexibility of product Gas Top Protectors application allows it to be used in almost all shapes and sizes of products, and the added value of Teflon spraying to the product far exceeds the value of non-stick coatings

In order to make up for the above-mentioned shortcomings of pure polytetrafluoroethylene and give full play to its advantages, some filling materials are often added in actual applications to improve its performance. In short, filled PTFE not only maintains its original excellent performance, but also improves its strength, hardness, and elasticity.

The linear expansion coefficient of pure PTFE at 20〜60℃ Poor thermal conductivity. can improve mechanical strength and thermal conductivity; filling glass fiber, asbestos, ceramics, etc. The friction coefficient of pure polytetrafluoroethylene is the smallest among solids at present, only 0.01%.

Usually referred to as 'Plastic King'; 3) The temperature resistance is also good, and it can work normally under the conditions of 80〜200℃; 4) The moisture absorption coefficient is small, and the water absorption rate is 0.

Pure PTFE seals have the following disadvantages: 1) The linear expansion coefficient is relatively large.47W; 3) It not only has cold fluidity, but also is prone to plastic deformation under high temperature and high pressure; 4) Poor mechanical strength, low hardness and low elasticity. It can resist various acid and alkali corrosion.Pure PTFE seals have the following advantages: 1)

Low friction coefficient. can increase resistance Abrasiveness and improve compression resistance, reduce shrinkage. The commonly used filling materials and their functions are: filling graphite and molybdenum disulfide can improve thermal conductivity and PTFE BBQ Grill Mesh Mat wear resistance; filling bronze, molybdenum, silver powder, etc. 2) It has a high degree of chemical stability..02〜0.